Process for the production of lanthanum chromite films by plasma spraying
US5332598A · kind A · utility
Assignee
Inventors
Key dates
| Filing date | Dec 2, 1992 |
| Grant date | Jul 26, 1994 |
| Priority date | — |
| Expiry date | Dec 2, 2012 |
Classification
- Technology area (CPC Y)Emerging Cross-Sectional Technologies
- CPC primaryY02P70/50
- WIPO fieldElectrical machinery, apparatus, energy
- WIPO sectorElectrical engineering
Abstract
A process for the production of a lanthanum chromite film, including the steps of preparing a plasma spray powder by mixing 1-15 parts by weight of powdery chromium oxide powder to 100 parts by weight of powdery lanthanum chromite, this lanthanum chromite having a composition ratio of A sites to B-sites being in a range of 1:1 to 1:0.9, forming a plasma sprayed film by plasma spraying the plasma spray powder onto a substrate, and forming the lanthanum chromite film by heat treating the resulting plasma sprayed film. The plasma spray powder may be produced by preparing a mixed powder by adding 1-15 parts by weight of powdery chromium oxide to 100 parts by weight of a synthesis powder capable of producing the lanthanum chromite film by heat treatment, the synthesis powder containing at least chromium oxide and lanthanum chromite and the lanthanum chromite film having a composition ratio of A-sites to B-sites being in a range of 1:1 to 1:0.9, obtaining a synthesized product by heating the mixed powder, and granulating the synthesized product.
Source: USPTO / EPO open patent data. Objective bibliographic and citation counts.