High strength hot rolled steel sheet having excellent bendability and method for manufacturing the same
US9200344B2 · kind B2 · utility
Assignee
Inventors
Key dates
| Filing date | Sep 15, 2011 |
| Grant date | Dec 1, 2015 |
| Priority date | — |
| Expiry date | Jan 18, 2032 |
Classification
- Technology area (CPC C)Chemistry; Metallurgy
- CPC primaryC21D2211/005
- WIPO fieldMaterials, metallurgy
- WIPO sectorChemistry
Abstract
A steel sheet including C at 0.05 to 0.15%, Si at 0.2 to 1.2%, Mn at 1.0 to 2.0%, P at not more than 0.04%, S at not more than 0.0030%, Al at 0.005 to 0.10%, N at not more than 0.005% and Ti at 0.03 to 0.13%, the balance being Fe and inevitable impurities, includes surface regions having an area fraction of bainite of less than 80% and an area fraction of a ferrite phase with a grain diameter of 2 to 15 μm of not less than 10%, the surface regions extending from both surfaces of the steel sheet each to a depth of 1.5 to 3.0% relative to a total sheet thickness, as well as an inner region other than the surface regions having an area fraction of a bainite phase of more than 95%, and has a tensile strength of not less than 780 MPa.
Source: USPTO / EPO open patent data. Objective bibliographic and citation counts.