Ti(C,N)-based cermet with Ni3Al and Ni as binder and preparation method thereof

US9222153B2 · kind B2 · utility

Assignee

• Huazhong University of Science and Technology · CN

Inventors

• Weihao XIONG · 红钢城街道, CN
• Bin Huang · Beijing, CN
• Qingqing YANG · 红钢城街道, CN
• Mingkun Chen · Cupertino, US
• Zhenhua YAO · 红钢城街道, CN
• Guopeng Zhang · Surrey, CA
• Xiao Ling Chen · Beijing, CN
• Shan Chen · Wuxi, CN

Key dates

• Filing date: Dec 31, 2014
• Grant date: Dec 29, 2015
• Expiry date: Dec 31, 2034

Classification

• Technology area (CPC C): Chemistry; Metallurgy
• CPC primary: C22C1/047
• WIPO field: Materials, metallurgy
• WIPO sector: Chemistry

Abstract

Provided are Ti(C,N)-based cermets with Ni3Al and Ni as binder and a preparation method thereof. The Ti(C,N)-based cermets are prepared by raw materials subjected to ball-mill mixing, die forming, vacuum degreasing and vacuum sintering, wherein weight percentage of each chemical component of the raw materials is as follows: TiC 34.2˜43%, TiN 8˜15%, Mo 10˜15%, WC 5˜10%, graphite 0.8˜1.0%, Ni 20˜24%, and Ni3Al powder containing B 6˜10%. Ni powder and Ni3Al powder containing B are used as binder. The Ti(C,N)-based cermets feature in excellent corrosion resistance, oxidation resistance and mechanical properties at high temperature, has a hardness of 89.0˜91.9 HRA, a room temperature bending strength of 1600 MPa or more, and a fracture toughness of 14 MPa·m1/2 or more, and is applicable for manufacturing high-speed cutting tools, dies and heat-resisting and corrosion-resisting components.